特性 |
|---|
| 熔融指數(shù) |
| 成型收縮率 |
| 拉伸強(qiáng)度 |
| 斷裂伸長(zhǎng)率 |
| 彎曲強(qiáng)度 |
| 彎曲模量 |
| 簡(jiǎn)支梁缺口沖擊 |
| 懸臂梁缺口沖擊 |
| 熱變形溫度 |
| 維卡軟化點(diǎn)溫度 |
| 阻燃性能 |
| 表面電阻率 |
| 體積電阻率 |
| 密度 |
|
測(cè)試標(biāo)準(zhǔn) |
|---|
| ASTM D1238 |
| ASTM D955 |
| ASTM D638 |
| ASTM D638 |
| ASTM D790 |
| ASTM D790 |
| ISO 179 |
| ASTM D256 |
| ASTM D648 |
| ASTMD1525 |
| UL 94 |
| IEC 60093 |
| IEC 60093 |
| ASTM D792 |
|
測(cè)試條件 |
|---|
| 300℃1.2kg |
| 3.2mm |
| 50mm/min |
| 50mm/min |
| 2mm/min |
| 2mm/min |
| 4mm |
| 3.2mm 23℃ |
| 1.82Mpa |
| 50N 120℃/h |
| 0.8mm |
| - |
| - |
| 23℃ |
|
單位 |
|---|
| g/10min |
| % |
| Mpa |
| % |
| Mpa |
| Mpa |
| KJ/㎡ |
| J/m |
| ℃ |
| ℃ |
| Class |
| Ω |
| Ω?m |
| kg/m3 |
|
PC5210 |
|---|
| 15 |
| 0.5-0.7 |
| 62 |
| 110 |
| 100 |
| 2500 |
| 58 |
| 500 |
| 97 |
| 111 |
| V-0 |
| 1.00E+16 |
| 1.00E+15 |
| 1190 |
|
PC5220 |
|---|
| 23 |
| 0.5-0.7 |
| 63 |
| 109 |
| 100 |
| 2500 |
| 58 |
| 500 |
| 96 |
| 110 |
| V-0 |
| 1.00E+16 |
| 1.00E+15 |
| 1190 |
- ●上述數(shù)據(jù)是用注塑樣品在23℃,濕度50%的條件下測(cè)得,數(shù)據(jù)為實(shí)驗(yàn)典型值,不作正式質(zhì)保承諾。
- ●顏色產(chǎn)品的數(shù)據(jù)可能略有變化
| 加工工藝 |
|---|
| PC5210 |
| PC5220 |
| 料筒溫度 射嘴 |
|---|
| 270~280℃ |
| 270~280℃ |
| 料筒溫度 前段 |
|---|
| 260~270℃ |
| 260~270℃ |
| 料筒溫度 中段 |
|---|
| 260~265℃ |
| 260~265℃ |
| 料筒溫度 后段 |
|---|
| 260~265℃ |
| 255~260℃ |
| 模具溫度 |
|---|
| 60~90℃ |
| 60~90℃ |
| 背壓壓力 |
|---|
| 0.35~1.00Mpa |
| 0.35~1.00Mpa |
| 螺桿速度 |
|---|
| 25-75Rpm |
| 25-75Rpm |
| 干燥溫度 |
|---|
| 100~120℃ |
| 100~120℃ |
| 干燥時(shí)間 |
|---|
| 2~3h |
| 2~3h |
- ●以上工藝參數(shù)僅供參考,具體要根據(jù)產(chǎn)品、注塑機(jī)和模具進(jìn)行適當(dāng)調(diào)整。